Product Description

Product Attributes

Model No.: PEEK Film (Polyetheretherketone) Film sold

Brand: HONYPLAS

Packaging & Delivery

Selling Units	:	Kilogram
Package Type	:	Export package

The file is encrypted. Please fill in the following information to continue accessing it

PEEK film production processing

PEEK block customized size



Product Description

PEEK film offers an outstanding range of physical, thermal, chemical & radiological properties. PEEK is a high performance semi-crystalline thermoplastic. PEEK's characteristics include high temperature performance, excellent wear properties, superior chemical resistance, hydrolytic stability and outstanding toughness and strength. PEEK meets many aerospace, automotive, fire, smoke and toxicity, food/water, medical/pharmaceutical, and military approvals and standards.

Peek Film 11 Jpeg

Size

Thicknesses between 10µm (0,01 mm) up to 1000µm (1 mm);

Width usually about 420mm, but customer preferences of special sizes or thicknesses will be provided.

Thin film critical characteristics HONYPLAS®PEEK Sheet Rod

The PEEK film manufactured by thermoplastic molding of the super engineering plastic PEEK resin is divided into two types: low crystallization and high crystallization. PEEK film has the following remarkable characteristics:

* Mechanical properties: A plastic film that has both toughness and rigidity and is balanced, and has extremely excellent fatigue resistance, which is comparable to alloy materials.

* High temperature resistance: It can withstand the temperature of lead-free soldering process. The RTI grade for non-impact mechanical applications is 220°C, and for electrical applications is 200°C. The carbonization point remains stable up to 500°C.

* Self-lubricating property: It has outstanding sliding properties and is suitable for applications that strictly require low friction coefficient and wear resistance, especially the PEEK film modified by mixing carbon fiber and graphite in a certain proportion has better self-lubricating performance.

* Chemical resistance (corrosion resistance): It has excellent chemical resistance. Among common chemicals, only concentrated sulfuric acid can dissolve or destroy it. Its corrosion resistance is similar to that of nickel steel.

* Flame retardant: very stable polymer, can reach high flame retardant standard without adding any flame retardant, halogen-free, in line with IEC 61249-2-21 standard.

* Stripping resistance: It has good stripping resistance, can be made into a thinly covered electromagnetic wire, and can be used under harsh conditions.

* Fatigue resistance: Excellent fatigue resistance.

* Radiation resistance: the ability to withstand high radiation is very strong, and it can still maintain good insulation ability under ultra-high radiation dose.

* Hydrolysis resistance: not affected by water and high-pressure water vapor, products made of this film material can still maintain excellent characteristics in continuous use in high-temperature and high-pressure water.

* Melt processability: fusion with metal when the temperature is above the melting point, easy ultrasonic sealing (PET film can also be sealed), laser can be melted and printed.

* High sound clarity: avoid the "hearing fatigue" caused by the noise of the metal film, and achieve better acoustic performance.

* Environmental protection and safety: lightweight, recyclable, compliant with RoHS standards, can be used to manufacture products that meet the requirements of the same directive, and meet the requirements of the US Food and Drug Administration (FDA).

* Wide range of thickness options: films with a thickness of 4~300μm can be produced, and can be customized according to customer needs.

Polyetheretherketone (PEEK) Sheet SPECIFICATION

产品名称 Product

颜色 Color

表面纹理 Texture

厚度Thickness(μm)

宽度Width(mm)

PEEK膜

棕黄色

Yellowish brown

光面/光面 Polished/Polished

光面/哑光 Polished/matte

哑光/哑光 matte/matte

4~100

≤650

100~300

≤1060

Polyetheretherketone bar TYPICAL PROPERTY VALUES

Technical Data Sheet of Amorphous PEEK Film：

	特性 Properties	测试方法 Test Method	单位 Units	测试值Value
物理性能 Physical Performance	密度 Density	ASTM D792	g/cm3	1.26
	吸水率 Moisture Absorption, 24h	ASTM D570	%	0.04
	热收缩率 Thermal Shrinking Rate	ISO 11501（200℃）	%	＜8
机械性能 Mechanical Performance	拉伸强度 Tensile Strength	ASTM D882	MD（MPa）	＞70
	拉伸强度 Tensile Strength	ASTM D882	TD（MPa）	＞70
	断裂伸长率 Elongation at Break	ASTM D882	MD %	＞150
	断裂伸长率 Elongation at Break	ASTM D882	TD %	＞150
	拉伸弹性模量 Tensile Modulus	ASTM D882	MD %	＞3000
	拉伸弹性模量 Tensile Modulus	ASTM D882	TD %	＞3000
耐温性能 Thermal Performance	熔点 Melting Point	ISO 11357	℃	343
	热膨胀系数 Coefficient of Thermal Expansion	ISO 11359(＜Tg)	ppm/K	40
	玻璃化温度 Glass Transition Temperature(Tg)	ISO 11357	℃	151
	热变形温度 Distortion Temperature	ASTM D648(0.45MPa)	℃	205
电气性能 Electrical properties	介电强度 Dielectric Strength(25μm)	ASTM D149	KV/mm	120
	体积电阻 Volume Resistivity@25℃,50%RH	ASTM D257	Ω·cm	1016
	介电常数 Dielectric Constant(Dk)	ASTM D150(@23℃，3GHz)		3.2
	介电损耗因子 Dielectric Dissipation Factor(Df)	ASTM D150(@23℃，3GHz)		0.004

Technical Data Sheet of Semi-crystalline PEEK Film：

	特性 Properties	测试方法 Test Method	单位 Units	测试值Value
物理性能 Physical Performance	密度 Density	ASTM D792	g/cm3	1.30
	吸水率 Moisture Absorption, 24h	ASTM D570	%	0.04
	热收缩率 Thermal Shrinking Rate	ISO 11501（200℃）	%	＜0.5
机械性能 Mechanical Performance	拉伸强度 Tensile Strength	ASTM D882	MD（MPa）	＞90
	拉伸强度 Tensile Strength	ASTM D882	TD（MPa）	＞90
	断裂伸长率 Elongation at Break	ASTM D882	MD %	＞120
	断裂伸长率 Elongation at Break	ASTM D882	TD %	＞120
	拉伸弹性模量 Tensile Modulus	ASTM D882	MD %	＞3000
	拉伸弹性模量 Tensile Modulus	ASTM D882	TD %	＞3000
耐温性能 Thermal Performance	熔点 Melting Point	ISO 11357	℃	343
	热膨胀系数 Coefficient of Thermal Expansion	ISO 11359(＜Tg)	ppm/K	40
	玻璃化温度 Glass Transition Temperature(Tg)	ISO 11357	℃	151
	热变形温度 Distortion Temperature	ASTM D648(0.45MPa)	℃	205
电气性能 Electrical properties	介电强度 Dielectric Strength(25μm)	ASTM D149	KV/mm	120
	体积电阻 Volume Resistivity@25℃,50%RH	ASTM D257	Ω·cm	1016
	介电常数 Dielectric Constant(Dk)	ASTM D150(@23℃，3GHz)		3.2
	介电损耗因子 Dielectric Dissipation Factor(Df)	ASTM D150(@23℃，3GHz)		0.004