TECAMID 66 natural PA 66 UNFILLED

Get Latest Price

Payment Type:	T/T,Paypal
Incoterm:	FOB,CFR,CIF,EXW,DDU
Min. Order:	1 Kilogram
Transportation:	Ocean,Land,Air,Express
Port:	Shenzhen,Guangzhou,Hongkong

Contact Now

Product Description

Product Attributes

Packaging & Delivery

Product Description

Product Attributes

Model No.: TECAMID 66 natural PA 66 UNFILLED

Brand: TECAMID

Packaging & Delivery

Selling Units	:	Kilogram
Package Type	:	Export package

The file is encrypted. Please fill in the following information to continue accessing it

HONY Plastics and Metal CNC machined workshop.mp4

Nylon bushing plain bush flange sleeves



Product Description

Polyamide 66 has good rigidity, hardness, abrasion resistance and thermal dimensional stability. In addition, nylon 66 has outstanding wear resistance and low frictional properties. It also has very good temperature, chemical, and impact properties. Users should be aware of PA 66 propensity to absorb moisture which could affect dimensional stability. In fact, PA 66 will tend to absorb more moisture at saturation than cast PA type 6. It has been successfully used in diverse applications ranging from electronics, marine, and automotive industries, to forrestry, construction and mining.

Tecamid 66 Natural Pa 66 Unfilled Jpg

FACTS

Chemical designation

PA 66 (Polyamide 66)

Colour

ivory

Density

1.15 g/cm3

MAIN FEATURES

good slide and wear properties

electrically insulating

good wear properties

good weldable and bondable

high strength

resistant to many oils, greases and fuels

high toughness

TARGET INDUSTRIES

mechanical engineering

food technology

electronics

aircraft and aerospace technology

automotive industry

TECAMID 66 natural PA 66 UNFILLED Technical Data Sheet

Mechanical Properties
VALUE	UNIT	PARAMETER	NORM
Modulus of elasticity	3500	MPa	1mm/min	DIN EN ISO 527-2
(tensile test)	3500	MPa	1mm/min	DIN EN ISO 527-2
Tensile strength	85	MPa	50mm/min	DIN EN ISO 527-2
Tensile strength at yield	84	MPa	50mm/min	DIN EN ISO 527-2
Elongation at yield (tensile test)	7	%	50mm/min	DIN EN ISO 527-2
Elongation at break (tensile test)	70	%	50mm/min	DIN EN ISO 527-2
Flexural strength	110	MPa	2mm/min, 10 N	DIN EN ISO 178
Modulus of elasticity	3100	MPa	2mm/min, 10 N	DIN EN ISO 178
(flexural test)	3100	MPa	2mm/min, 10 N	DIN EN ISO 178
Compression modulus	2700	MPa	5mm/min, 10 N	EN ISO 604
Impact strength (Charpy)	n.b.	kJ/m2	max. 7,5J	DIN EN ISO 179-1eU
Notched impact strength (Charpy)	5	kJ/m2	max. 7,5J	DIN EN ISO 179-1eA
Ball indentation hardness	175	MPa		ISO 2039-1
Compression strength	20/35/81	MPa	1% / 2% / 5%	EN ISO 604
Thermal Prpperties
ROPERTIES	VALUE	UNIT	PARAMETER	NORM
Glass transition temperature	47	C		DIN EN ISO 11357
Melting temperature	258	C		DIN EN ISO 11357
Thermal conductivity	0.36	W/(k*m)		ISO 22007-4:2008
Specific heat	1.5	J/(g*K)		ISO 22007-4:2008
Service temperature	170	C	short term	NN
Service temperature	100	C	long term	NN
Thermal expansion (CLTE)	11	10-5*1/K	23-60℃, long.	DIN EN ISO 11359-1;2
Thermal expansion (CLTE)	12	10-5*1/K	23-100℃, long.	DIN EN ISO 11359-1;2
Electrical Properties
ROPERTIES	VALUE	UNIT	PARAMETER	NORM
surface resistivity	1014	Ω		-
volume resistivity	1014	Ω
Other Properties
VALUE	UNIT	PARAMETER	NORM
Resistance to hot water/ bases	(+)	-		-
Flammability (UL94)	HB	-	corresponding to	DIN IEC 60695-11-10;
Resistance to weathering	-	-		-
Water absorption	0.2 - 0.4	%	24h / 96h (23°C)	DIN EN ISO 62